AMS 4924 Chemical composition and Mechanical properties
| AISI 1010 steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round or thickness | |
|---|---|
| Categories: | Metal; Ferrous Metal; Carbon Steel; AISI 1000 Series Steel; Low Carbon steel |
| Material Notes: | Easily cold formed by heading, extruding, upsetting, bending, and other deforming processes. Uses for wires include electroplated products, such as racks, storage bins, shopping carts, fan guards, and jewelry, and unplated such as wires, staples, hardware, and barbed wire. |
| Key Words: | UNS G10100, AMS 5040, AMS 5042, AMS 5044, AMS 5047, AMS 5053, ASTM A29, ASTM A108, ASTM A510, ASTM A519, ASTM A545, ASTM A549, ASTM A575, ASTM A576, MIL SPEC MIL-S-11310 (CS1010), JIS S 9 CK, SAE J403, SAE J412, SAE J414, DIN 1.1121, AFNOR XC 10 (Fr), JIS S10 C, JIS S 12 C |
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 7.87 g/cc | 0.284 lb/in³ | Typical for steel |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Brinell | 95 | 95 | |
| Hardness, Knoop | 113 | 113 | Converted from Brinell hardness. |
| Hardness, Rockwell B | 55 | 55 | Converted from Brinell hardness. |
| Hardness, Vickers | 98 | 98 | Converted from Brinell hardness. |
| Tensile Strength, Ultimate | 325 MPa | 47100 psi | |
| Tensile Strength, Yield | 180 MPa | 26100 psi | |
| Elongation at Break | 28.0 % | 28.0 % | in 50 mm |
| Reduction of Area | 50.0 % | 50.0 % | |
| Modulus of Elasticity | 200 GPa | 29000 ksi | Typical for steel |
| Bulk Modulus | 140 GPa | 20300 ksi | Typical for steel |
| Poissons Ratio | 0.290 | 0.290 | Typical For Steel |
| Machinability | 55 % | 55 % | Based on AISI 1212 steel. as 100% machinability. The machinability of Group I bar, rod, and wire products can be improved by cold drawing. |
| Shear Modulus | 80.0 GPa | 11600 ksi | Typical for steel |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 0.0000143 ohm-cm | 0.0000143 ohm-cm | condition unknown |
| Thermal Properties | Metric | English | Comments |
| CTE, linear |
12.2 µm/m-°C @Temperature 0.000 - 100 °C |
6.78 µin/in-°F @Temperature 32.0 - 212 °F |
|
|
13.0 µm/m-°C @Temperature 0.000 - 200 °C |
7.22 µin/in-°F @Temperature 32.0 - 392 °F |
||
|
13.5 µm/m-°C @Temperature 0.000 - 300 °C |
7.50 µin/in-°F @Temperature 32.0 - 572 °F |
||
|
13.8 µm/m-°C @Temperature 0.000 - 400 °C |
7.67 µin/in-°F @Temperature 32.0 - 752 °F |
||
|
14.2 µm/m-°C @Temperature 0.000 - 500 °C |
7.89 µin/in-°F @Temperature 32.0 - 932 °F |
||
|
14.6 µm/m-°C @Temperature 0.000 - 600 °C |
8.11 µin/in-°F @Temperature 32.0 - 1110 °F |
||
|
14.9 µm/m-°C @Temperature 0.000 - 700 °C |
8.28 µin/in-°F @Temperature 32.0 - 1290 °F |
||
| Specific Heat Capacity | 0.448 J/g-°C | 0.107 BTU/lb-°F | condition unknown; 50-100°C (122-212°F) |
|
0.498 J/g-°C @Temperature 150 - 200 °C |
0.119 BTU/lb-°F @Temperature 302 - 392 °F |
||
|
0.519 J/g-°C @Temperature 200 - 250 °C |
0.124 BTU/lb-°F @Temperature 392 - 482 °F |
||
|
0.536 J/g-°C @Temperature 250 - 300 °C |
0.128 BTU/lb-°F @Temperature 482 - 572 °F |
||
|
0.565 J/g-°C @Temperature 300 - 350 °C |
0.135 BTU/lb-°F @Temperature 572 - 662 °F |
||
|
0.590 J/g-°C @Temperature 350 - 400 °C |
0.141 BTU/lb-°F @Temperature 662 - 752 °F |
||
|
0.649 J/g-°C @Temperature 400 - 450 °C |
0.155 BTU/lb-°F @Temperature 752 - 842 °F |
||
|
0.729 J/g-°C @Temperature 550 - 600 °C |
0.174 BTU/lb-°F @Temperature 1020 - 1110 °F |
||
|
0.825 J/g-°C @Temperature 650 - 700 °C |
0.197 BTU/lb-°F @Temperature 1200 - 1290 °F |
||
| Thermal Conductivity | 51.9 W/m-K | 360 BTU-in/hr-ft²-°F | Typical steel |
| Component Elements Properties | Metric | English | Comments |
| Carbon, C | 0.080 - 0.13 % | 0.080 - 0.13 % | |
| Iron, Fe | 99.18 - 99.62 % | 99.18 - 99.62 % | As remainder |
| Manganese, Mn | 0.30 - 0.60 % | 0.30 - 0.60 % | |
| Phosphorous, P | <= 0.040 % | <= 0.040 % | |
| Sulfur, S | <= 0.050 % | <= 0.050 % | |
Users viewing this material also viewed the following:
AISI 1010 Steel, cold drawn
AISI 1010 Steel, cold drawn bar, 19-32 mm (0.75-1.25 in) round or thickness
AISI 1010 Steel, CQ sheet,1.6-5.8 mm round or thickness
AISI 1008 Steel, hot rolled bar, 19-32 mm (0.75-1.25 in) round
AISI 1008 Steel, cold drawn bar, 19-32 mm (0.75-1.25 in) round
M1010B / 6783