Ti 10-2-3 Ti Alloy

Data Table for:Ti Alloy:Ti 10-2-3 Ti Alloy

Steel grade type	Ti Alloy:
Standard
Production specifications	Steel plate,Sheet, Coil,Flat bar,Round bar, Strip steel,wire,All kinds of forgings.
Mchining	Turning Milling Grinding Deep hole drilling: length max 9.8 meters.
Range of work	Round bar steel: 1mm to 2000mm Square-shape steel: 10mm to 1000mm steel Plate/sheet:0.08mm to 800mm Width: 10mm to 1500mm Lenth: We can supply any lenth based on the customer's requirement. Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes Tubings: OD: φ4-410 mm, with wall thickness ranging from 1-35 mm.
Heat treatment	Normalizing,Annealing,Tempering,Quenching,Hardening and tempering,Seasoning,Surface hardening,Carburizing

Ti 10-2-3 Ti Alloy Chemical composition and Mechanical properties

Our to produce better steel-based products are the main used in industrial manufacturing various types Ti AlloyTi 10-2-3 plate,Ti 10-2-3 Round Bar,Ti 10-2-3 forgings,Ti 10-2-3 suppliers, Ti 10-2-3 Stock,Ti 10-2-3 sheet, Ti 10-2-3 flat bar, Ti 10-2-3 pipe,Ti 10-2-3 tube,Ti 10-2-3 mould,Ti 10-2-3 round ingot,Ti 10-2-3 cold-rolled steel,Ti 10-2-3 coil,Ti 10-2-3 strap steel,Ti 10-2-3 hot-rolled steel,Ti 10-2-3 medium plate, Ti 10-2-3 heavy plate,Ti 10-2-3 shapped bar,Ti 10-2-3 hexahedral bar,Ti 10-2-3,Ti 10-2-3 slab ingot,Ti 10-2-3 slab,Ti 10-2-3 price,Ti 10-2-3 square bar,Ti 10-2-3 square steel,Ti 10-2-3 wire.Extending the industrial all kinds of mechanical industrial parts machining and, at the same time, using fine heat treatment process,tempering,hardening,heating,bright annealing,rotary hearth.chemical composition and Improving mechanical properties of Ti 10-2-3.

Ti 10-2-3 Ti Alloy

Our advantages

Ti 10-2-3 properties and heat treatment forged piece, Including Ti 10-2-3 application and specifications, We have all specifications，Including Ti 10-2-3 steel plate, Ti 10-2-3 sheet, Ti 10-2-3 square steel, Ti 10-2-3 flat bar,Ti 10-2-3 round bar,Ti 10-2-3 forgings, we can own production and sales.

Introduction to Our Products:

Specialized high quality steel

We have the advantages of equipment, technologies and price

forged/hot rolling/ extrusion of steel

We can produce the Ti 10-2-3 has the following specifications:

Round bar steel: 1mm to 3000mm

Square-shape steel: 1mm to 2000mm

Plate steel:0.1mm to 2500mm

Width: 10mm to 2500mm

Lenth: We can supply any lenth based on the customer's requirement.

Forging: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

Tubings: OD: φ6-219 mm, with wall thickness ranging from 1-35 mm.

Finished goods condition: hot forging/hot rolling + annealing/normalizing + tempering/quenching + tempering/any conditions based on the customer's requirement

Surface conditions: scaled (hot working finish)/ground/rough machining/fine machining/based on the customer's requirement

Furnaces for metallurgical processing: electrode arc + LF/VD/VOD/ESR/Vacuum consumable electrode.

Ultrasonic inspection: 100% ultrasonic inspection for any inperfections or based on the customer's requirementExcellent service for all kinds of industries,with advantages of technologies, equipment and price.

We serve you with our honesty, integrity, and professionality.

Chemical composition % of the ladle analysis of grade Ti 10-2-3 and Standards

Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) Solution Treated 850°C (1560°F)
Categories: Metal; Nonferrous Metal; Titanium Alloy; Beta Titanium Alloy

Material Notes: 5 other heat treatments of this alloy are in MatWeb.

Key Words: KS 10-2-3; Ti 10-2-3; TIMETAL 10-2-3

Physical Properties	Metric	English	Comments
Density	4.65 g/cc	0.168 lb/in³

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	1000 MPa	145000 psi
Tensile Strength, Yield	930 MPa	135000 psi
Elongation at Break	17.0 %	17.0 %
Modulus of Elasticity	110 GPa	16000 ksi	unspecified heat treatment
Poissons Ratio	0.330	0.330	Typical for beta titanium alloy.
Fracture Toughness	110 MPa-m½	100 ksi-in½	K(IC)
Shear Modulus	41.0 GPa	5950 ksi

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.000150 ohm-cm	0.000150 ohm-cm	Estimated from similar high-V-stabilized beta titanium alloys.

Thermal Properties	Metric	English	Comments
CTE, linear	9.70 µm/m-°C @Temperature 20.0 - 100 °C	5.39 µin/in-°F @Temperature 68.0 - 212 °F
	9.70 µm/m-°C @Temperature 20.0 - 425 °C	5.39 µin/in-°F @Temperature 68.0 - 797 °F	average after ST 760ºC; Age 525ºC
Specific Heat Capacity	0.525 J/g-°C	0.125 BTU/lb-°F	Typical value for titanium alloys.
Thermal Conductivity	7.80 W/m-K	54.1 BTU-in/hr-ft²-°F	Estimated from similar high-V-stabilized beta titanium alloys.
Maximum Service Temperature, Air	315 °C	599 °F
Beta Transus	760 °C	1400 °F

Component Elements Properties	Metric	English	Comments
Aluminum, Al	2.60 - 3.40 %	2.60 - 3.40 %
Carbon, C	<= 0.0500 %	<= 0.0500 %
Hydrogen, H	<= 0.0150 %	<= 0.0150 %
Iron, Fe	1.60 - 2.20 %	1.60 - 2.20 %
Nitrogen, N	<= 0.0500 %	<= 0.0500 %
Other, each	<= 0.100 %	<= 0.100 %
Other, total	<= 0.300 %	<= 0.300 %
Oxygen, O	<= 0.130 %	<= 0.130 %
Titanium, Ti	82.855 - 86.8 %	82.855 - 86.8 %	As Balance; Elemental Compostions per ASTM B265
Vanadium, V	9.00 - 11.0 %	9.00 - 11.0 %

Users viewing this material also viewed the following:
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 760°C, Aged 385°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 760°C; Age 525°C (980°F)
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 815°C, Anneal 620°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3) ST 730°C; overage 580°C
Titanium Ti-10V-2Fe-3Al (Ti 10-2-3), Anneal 1 hr. 760°C

MTB020 / 14144

Machining performance

Download Ti 10-2-3 the mechanical properties of the report, the report provides detailed performance analysis and application. Download >>

Principal Design Features

One of the most widely used precipitation hardening grades in the business. While soft and ductile in the solution annealed condition, it is capable of high properties with a single precipitation or aging treatment. Characterized by good corrosion resistance, high harness, toughness and strength.

Machinability

Long, gummy chips characterize this alloys machinability. It can be machined in the annealed condition, however condition H1150M will yield best results. Post machining solution treatment of parts will be required prior to final hardening if machining in this condition.

Heat Treatment

CONDITION A--Soak at 1900 F (1038 C) for 30 minutes and cool below 60 F (16 C) for complete martensite transformation. CONDITION H 950- Treat Condition A material at 900 F(482 C) for 1 hour, air cool.. CONDITION H925, H1025, H1075, H1100, H1150- Soak solution treated material for 4 hours at specified temperature, air cool, CONDITION H1150M- Soak solution treated material at 1400 F (760 C) for 2 hours, air cool, then re-heat to 1150 F (620 C) for 4 hours and air cool.

Welding

Successfully welded by common fusion and resistance methods, this alloy should not be joined by oxyacetylene welding. AWS E/ER630 filler metal is recommended if required.

Forging

Soak for 1 hour at 2150 F (1177 C) prior to forging. Do not work below 1850 F (1010 C). Post-work solution treatment is required prior to final hardening.

Hot tags:Ti 10-2-3 steel plate, Ti 10-2-3 sheet, Ti 10-2-3 square steel, Ti 10-2-3 flat bar,Ti 10-2-3 round bar,Ti 10-2-3 forgings

关闭提示关闭

确认取消

Mechanical Properties

Properties		Conditions
Properties		T (°C)	Treatment
Density (×1000 kg/m3)	7.7-8.03	25
Poisson's Ratio	0.27-0.30	25
Elastic Modulus (GPa)	190-210	25
Tensile Strength (Mpa)	1158	25	oil quenched, fine grained, tempered at 425°C
Yield Strength (Mpa)	1034
Elongation (%)	15
Reduction in Area (%)	53
Hardness (HB)	335	25	oil quenched, fine grained, tempered at 425°C

Thermal Properties

Properties		Conditions
Properties		T (°C)	Treatment
Thermal Conductivity (W/m-K)	42.7	100
Specific Heat (J/kg-K)	477	50-100

Physical Properties

Quantity	Value	Unit
Thermal expansion	16 - 17	e-6/K
Thermal conductivity	16 - 16	W/m.K
Specific heat	500 - 500	J/kg.K
Melting temperature	1370 - 1400	°C
Service temperature	0 - 500	°C
Density	8000 - 8000	kg/m3
Resistivity	0.7 - 0.7	Ohm.mm2/m

Hot keywords:Ti 10-2-3

Previous page:Ti-5-5-2-3 Ti Alloy
Next pageTitanium 1100 Ti Alloy

Favorite

Ti 10-2-3 Ti Alloy

Data Table for:Ti Alloy:Ti 10-2-3 Ti Alloy

Ti 10-2-3 Ti Alloy Chemical composition and Mechanical properties

Ti 10-2-3 Ti Alloy

关闭提示 关闭

Mechanical Properties

Thermal Properties

Physical Properties

Further reading:

关闭提示关闭