A 1028 S42225


A 1028 S42225 material is SAE A 1028 (2009) Stainless Steel Bars for Compressor and Turbine Airfoils Stainless Steel Bars for Compressor and Turbine Airfoils.

Chemical composition of A 1028 S42225, A 1028 S42225 mechanical properties, A 1028 S42225 datasheet, A 1028 S42225 equivalent grade, Heat treatment and temperature process of A 1028 S42225.


A 1028 S42225 property sheet

A 1028 S42225 Spec.

SAE A 1028 (2009)
Stainless Steel Bars for Compressor and Turbine Airfoils

Chemical Composition of A 1028 S42225

C: Max 0.22
Si: Max 0.40
Mn: Max 0.75
P: Max Min
S: Max Min
Ni: Max 0.75
Cr: Max 12.50
Al: Max Min
Cu: Max Min
Ti: Max Min
Fe: Max remaining
N: Max Min
Mo: Max 1.00
W: Max 1.00
V: Max 0.22

Mechanical Properties of A 1028 S42225

Rp0.2 (MPa) 323 (≥)
Rm (MPa) 357 (≥)
AKV (J) 24
A (%) 14
Z (%) 32
Hardness HBW 132

A 1028 S42225 shape and dimensions

A 1028 S42225 Round bar: 1mm-800mm
A 1028 S42225 Square bar: 10mm * 10mm-600mm *600mm
A 1028 S42225 Flat bar: Thickness:8mm-800mm Width:10mm to 1500mm
A 1028 S42225 Sheet or Plate: Thickness:3mm-80mm Width:1.5mm to 1500mm
A 1028 S42225 Strip or Coil: Thickness:0.1mm-3mm Width:1.5mm-1500mm
A 1028 S42225 Forgings: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes

A 1028 S42225 Stock

422 Stainless Steel|Alloy 422|UNS S42200|616|B4B Stock

A 1028 S42225 Relevant products

Stainless Steel 422|Alloy 422|S42200|616|B4B

Stainless Steel 422|Alloy 422|S42200|616|B4B

Stainless Steel 422 Alloy 422 AMS 5655 UNS S42200 616 B4B
UNS S42200 Round Bar

UNS S42200 Round Bar

Stainless Steel 422 Alloy 422 AMS 5655 UNS S42200 616 B4B
422(UNS S42200, 616, 1.4935) Stainless Steel Bar

422(UNS S42200, 616, 1.4935) Stainless Steel Bar

422(UNS S42200, 616, 1 4935) Stainless Steel BarAlloy 4...
422 Stainless Steel Round Bar

422 Stainless Steel Round Bar

422 Stainless Steel Round Bar is a hardenable, martensi...