J 2614
J 2614 material is UNS SAE J 2614 (2009) Welded and Cold-Drawn, High Strength (500 MPa Tensile Strength) Low Alloy Steel Hydraulic Tubing, Sub-Critically Annealed for Bending and Flaring Welded and Cold-Drawn, High Strength (500 MPa Tensile Strength) Low Alloy Steel Hydraulic Tubing, Sub-Critically Annealed for Bending and Flaring.
Chemical composition of J 2614, J 2614 mechanical properties, J 2614 datasheet, J 2614 equivalent grade, Heat treatment and temperature process of J 2614.
J 2614 property sheet
J 2614 Spec.
| UNS SAE J 2614 (2009) Welded and Cold-Drawn, High Strength (500 MPa Tensile Strength) Low Alloy Steel Hydraulic Tubing, Sub-Critically Annealed for Bending and Flaring |
Related Materials
| A 240 S44627 |
| A 268 S44627 |
| A 276 S44627 |
| S44627 |
| SA-240 S44627 |
| SA-268 S44627 |
| 2618 |
| 2618 |
| 2618 |
| 2618 |
| 2618 |
| 2618 |
| 9261 |
| 9261 |
| A 213 S32615 |
| A 322 6118 |
| A 322 6150 |
| A 322 61L18 |
| A 322 61L50 |
| A 400 9261 |
Chemical Composition of J 2614
| C: | Max | 0.06 |
| Si: | Max | 0.75 |
| Mn: | Max | 0.75 |
| P: | Max | Min |
| S: | Max | Min |
| Ni: | Max | 0.50 |
| Cr: | 25.00 | 27.00 |
| Al: | Max | Min |
| Cu: | Max | 0.20 |
| Ti: | Max | Min |
| Fe: | Max | Min |
| N: | Max | 0.04 |
| Mo: | 0.75 | 1.50 |
Mechanical Properties of J 2614
| Rp0.2 (MPa) | 674 (≥) |
| Rm (MPa) | 151 (≥) |
| AKV (J) | 12 |
| A (%) | 23 |
| Z (%) | 33 |
| Hardness | HBW 123 |
J 2614 shape and dimensions
| J 2614 Round bar: | 1mm-800mm |
| J 2614 Square bar: | 10mm * 10mm-600mm *600mm |
| J 2614 Flat bar: | Thickness:8mm-800mm Width:10mm to 1500mm |
| J 2614 Sheet or Plate: | Thickness:3mm-80mm Width:1.5mm to 1500mm |
| J 2614 Strip or Coil: | Thickness:0.1mm-3mm Width:1.5mm-1500mm |
| J 2614 Forgings: | Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes |