SB-446 N06625 Grade 2
SB-446 N06625 Grade 2 material is AMS SB-446 Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650) Rod and Bar Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650) Rod and Bar.
Chemical composition of SB-446 N06625 Grade 2, SB-446 N06625 Grade 2 mechanical properties, SB-446 N06625 Grade 2 datasheet, SB-446 N06625 Grade 2 equivalent grade, Heat treatment and temperature process of SB-446 N06625 Grade 2.
SB-446 N06625 Grade 2 property sheet
SB-446 N06625 Grade 2 Spec.
| AMS SB-446 Nickel-Chromium-Molybdenum-Columbium Alloy (UNS N06625), Nickel-Chromium-Molybdenum-Silicon Alloy (UNS N06219), and Nickel-Chromium-Molybdenum-Tungsten Alloy (UNS N06650) Rod and Bar |
Related Materials
Chemical Composition of SB-446 N06625 Grade 2
| C: | Max | 0.01 |
| Si: | Max | 0.05 |
| Mn: | Max | 1.50 |
| P: | Max | 0.04 |
| S: | Max | 0.01 |
| Ni: | Max | remaining |
| Cr: | 0.50 | 1.50 |
| Al: | 0.10 | 0.50 |
| Cu: | Max | 0.50 |
| Ti: | Max | Min |
| Fe: | 1.00 | 6.00 |
| Mo: | 26.00 | 30.00 |
| Co: | Max | 2.50 |
Mechanical Properties of SB-446 N06625 Grade 2
| Rp0.2 (MPa) | 787 (≥) |
| Rm (MPa) | 161 (≥) |
| AKV (J) | 43 |
| A (%) | 41 |
| Z (%) | 11 |
| Hardness | HBW 423 |
SB-446 N06625 Grade 2 shape and dimensions
| SB-446 N06625 Grade 2 Round bar: | 1mm-800mm |
| SB-446 N06625 Grade 2 Square bar: | 10mm * 10mm-600mm *600mm |
| SB-446 N06625 Grade 2 Flat bar: | Thickness:8mm-800mm Width:10mm to 1500mm |
| SB-446 N06625 Grade 2 Sheet or Plate: | Thickness:3mm-80mm Width:1.5mm to 1500mm |
| SB-446 N06625 Grade 2 Strip or Coil: | Thickness:0.1mm-3mm Width:1.5mm-1500mm |
| SB-446 N06625 Grade 2 Forgings: | Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes |