17-4PH

17-4PH material is ASTM SAE AMS 5342E (2006) Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4) ASTM SAE AMS 5343E (2006) Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1000) 150 ksi (1034 MPa) Tensile Strength (17-4) ASTM SAE AMS 5344F (2007) Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength (17-4) ASTM SAE AMS 5604G (2013) Steel, Corrosion Resistant, Sheet, Strip, and Plate 16.5Cr - 4.0Ni - 4.0Cu - 0.30Cb Solution Heat Treated, Precipitation Hardenable ASTM SAE AMS 5622F (2013) Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardenable Consumable Electrode Remelted ASTM SAE AMS 5643/H1150 (2013) Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing and Rings 16Cr – 4.0Ni – 0.30Cb (Nb) – 4.0Cu Solution and Precipitation Heat Treated (H1150) ASTM SAE AMS 5643S (2013) Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardenable Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4).

Chemical composition of 17-4PH, 17-4PH mechanical properties, 17-4PH datasheet, 17-4PH equivalent grade, Heat treatment and temperature process of 17-4PH.

Tags: 17-4PH,

17-4PH property sheet

17-4PH Spec.

ASTM SAE AMS 5342E (2006)
Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1100) 130 ksi (896 MPa) Tensile Strength (17-4)

ASTM SAE AMS 5343E (2006)
Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb (Nb) - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H1000) 150 ksi (1034 MPa) Tensile Strength (17-4)

ASTM SAE AMS 5344F (2007)
Steel, Corrosion-Resistant, Investment Castings 16Cr - 4.1Ni - 0.28Cb - 3.2Cu Homogenization, Solution, and Precipitation Heat Treated (H900) 180 ksi (1241 MPa) Tensile Strength (17-4)

ASTM SAE AMS 5604G (2013)
Steel, Corrosion Resistant, Sheet, Strip, and Plate 16.5Cr - 4.0Ni - 4.0Cu - 0.30Cb Solution Heat Treated, Precipitation Hardenable

ASTM SAE AMS 5622F (2013)
Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardenable Consumable Electrode Remelted

ASTM SAE AMS 5643/H1150 (2013)
Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing and Rings 16Cr – 4.0Ni – 0.30Cb (Nb) – 4.0Cu Solution and Precipitation Heat Treated (H1150)

ASTM SAE AMS 5643S (2013)
Steel, Corrosion-Resistant, Bars, Wire, Forgings, Tubing, and Rings 16Cr - 4.0Ni - 0.30Cb - 4.0Cu Solution Heat Treated, Precipitation Hardenable

Related Materials

F738 Class P1-90 S17400

F836 Class P1-90 S17400

17-4PH, 1.4542, X5CrNiCuNb16-4

Chemical Composition of 17-4PH

C:	Max	0.07
Si:	Max	1.00
Mn:	Max	1.00
Cr:	15.00	17.50
Ni:	3.00	5.00
Cu:	3.00	5.00
Nb:	0.15	1.45

Mechanical Properties of 17-4PH

R_p0.2 (MPa)	626 (≥)
R_m (MPa)	755 (≥)
AKV (J)	33
A (%)	42
Z (%)	12
Hardness	HBW 344

17-4PH shape and dimensions

17-4PH Round bar:	1mm-800mm
17-4PH Square bar:	10mm * 10mm-600mm *600mm
17-4PH Flat bar:	Thickness:8mm-800mm Width:10mm to 1500mm
17-4PH Sheet or Plate:	Thickness:3mm-80mm Width:1.5mm to 1500mm
17-4PH Strip or Coil:	Thickness:0.1mm-3mm Width:1.5mm-1500mm
17-4PH Forgings:	Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes