A 193 B8M2 Class 2
A 193 B8M2 Class 2 material is SAE A 193/A 193M (2012) Standard Specification for Alloy-Steel and Stainless Steel Bolting for High Temperature or High Pressure Service and Other Special Purpose Applications Standard Specification for Alloy-Steel and Stainless Steel Bolting for High Temperature or High Pressure Service and Other Special Purpose Applications.
Chemical composition of A 193 B8M2 Class 2, A 193 B8M2 Class 2 mechanical properties, A 193 B8M2 Class 2 datasheet, A 193 B8M2 Class 2 equivalent grade, Heat treatment and temperature process of A 193 B8M2 Class 2.
A 193 B8M2 Class 2 property sheet
A 193 B8M2 Class 2 Spec.
| SAE A 193/A 193M (2012) Standard Specification for Alloy-Steel and Stainless Steel Bolting for High Temperature or High Pressure Service and Other Special Purpose Applications |
Related Materials
| A 193 B8M2 Class 2 |
| A 193 B8M2 Class 2B |
| B 388 TM22 |
| B 883 MIM-2200 |
| SA-193 Grade B8M2 Class 2B |
Chemical Composition of A 193 B8M2 Class 2
| C: | Max | 0.13 |
| Si: | Max | Min |
| Mn: | Max | Min |
| Ni: | Max | Min |
| Cr: | Max | 5.70 |
| Al: | Max | 6.30 |
| Cu: | Max | Min |
| Ti: | Max | Min |
| Fe: | Max | Min |
| Mo: | Max | 2.00 |
| Co: | Max | Min |
| Ta: | Max | 3.00 |
| Zr: | Max | 0.60 |
| W: | Max | 11.00 |
Mechanical Properties of A 193 B8M2 Class 2
| Rp0.2 (MPa) | 266 (≥) |
| Rm (MPa) | 874 (≥) |
| AKV (J) | 31 |
| A (%) | 41 |
| Z (%) | 14 |
| Hardness | HBW 412 |
A 193 B8M2 Class 2 shape and dimensions
| A 193 B8M2 Class 2 Round bar: | 1mm-800mm |
| A 193 B8M2 Class 2 Square bar: | 10mm * 10mm-600mm *600mm |
| A 193 B8M2 Class 2 Flat bar: | Thickness:8mm-800mm Width:10mm to 1500mm |
| A 193 B8M2 Class 2 Sheet or Plate: | Thickness:3mm-80mm Width:1.5mm to 1500mm |
| A 193 B8M2 Class 2 Strip or Coil: | Thickness:0.1mm-3mm Width:1.5mm-1500mm |
| A 193 B8M2 Class 2 Forgings: | Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes |