A 565 S41800


A 565 S41800 material is SAE A 565/A 565M (2010) Martensitic Stainless Steel Bars for High-Temperature Service Martensitic Stainless Steel Bars for High-Temperature Service.

Chemical composition of A 565 S41800, A 565 S41800 mechanical properties, A 565 S41800 datasheet, A 565 S41800 equivalent grade, Heat treatment and temperature process of A 565 S41800.


A 565 S41800 property sheet

A 565 S41800 Spec.

SAE A 565/A 565M (2010)
Martensitic Stainless Steel Bars for High-Temperature Service

Chemical Composition of A 565 S41800

C: 0.15 0.20
Mn: Max 0.50
Si: Max 0.50
P: Max 0.04
S: Max 0.03
Cr: 12.00 14.00
Ni: 1.80 2.20
Mo: Max Min
W: 2.50 3.50

Mechanical Properties of A 565 S41800

Rp0.2 (MPa) 145 (≥)
Rm (MPa) 482 (≥)
AKV (J) 14
A (%) 23
Z (%) 23
Hardness HBW 141

A 565 S41800 shape and dimensions

A 565 S41800 Round bar: 1mm-800mm
A 565 S41800 Square bar: 10mm * 10mm-600mm *600mm
A 565 S41800 Flat bar: Thickness:8mm-800mm Width:10mm to 1500mm
A 565 S41800 Sheet or Plate: Thickness:3mm-80mm Width:1.5mm to 1500mm
A 565 S41800 Strip or Coil: Thickness:0.1mm-3mm Width:1.5mm-1500mm
A 565 S41800 Forgings: Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes