B 637 N07750 Type 2
B 637 N07750 Type 2 material is ASTM B 637 (2012) Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service.
Chemical composition of B 637 N07750 Type 2, B 637 N07750 Type 2 mechanical properties, B 637 N07750 Type 2 datasheet, B 637 N07750 Type 2 equivalent grade, Heat treatment and temperature process of B 637 N07750 Type 2.
B 637 N07750 Type 2 property sheet
B 637 N07750 Type 2 Spec.
| ASTM B 637 (2012) Precipitation-Hardening and Cold Worked Nickel Alloy Bars, Forgings, and Forging Stock for Moderate or High Temperature Service |
Related Materials
| 2.4669 |
| NiCr15Fe7TiAl |
| N07750 |
| B 637 N07750 Type 1 |
| B 637 N07750 Type 2 |
| SB-637 N07750 Type 1 |
| Inconel X750 |
| N07750 |
| NiCr15Fe7TiAl |
Chemical Composition of B 637 N07750 Type 2
| C: | Max | 0.08 |
| Mn: | Max | 1.0 |
| Si: | Max | 0.5 |
| S: | Max | 0.01 |
| P: | Max | 0.015 |
| Cu: | Max | 0.5 |
| Fe: | 5.0 | 9.0 |
| Co: | Max | 1.0 |
| Nb: | 0.70 | 1.20 |
| Cr: | 14.0 | 17.0 |
| Ni: | 70 | Min |
| Al: | 0.40 | 1.00 |
| Ti: | 2.25 | 2.75 |
Mechanical Properties of B 637 N07750 Type 2
| Rp0.2 (MPa) | 641 (≥) |
| Rm (MPa) | 554 (≥) |
| AKV (J) | 23 |
| A (%) | 41 |
| Z (%) | 31 |
| Hardness | HBW 214 |
B 637 N07750 Type 2 shape and dimensions
| B 637 N07750 Type 2 Round bar: | 1mm-800mm |
| B 637 N07750 Type 2 Square bar: | 10mm * 10mm-600mm *600mm |
| B 637 N07750 Type 2 Flat bar: | Thickness:8mm-800mm Width:10mm to 1500mm |
| B 637 N07750 Type 2 Sheet or Plate: | Thickness:3mm-80mm Width:1.5mm to 1500mm |
| B 637 N07750 Type 2 Strip or Coil: | Thickness:0.1mm-3mm Width:1.5mm-1500mm |
| B 637 N07750 Type 2 Forgings: | Shafts with flanks/pipes/tubes/slugs/donuts/cubes/other shapes |